Communications - Scientific Letters of the University of Zilina 2016, 18(4):99-102 | DOI: 10.26552/com.C.2016.4.99-102

Corrosion Resistance of Hsla Steel after Various Surface Treatments in Chloride Environment

Kamil Borko¹, Filip Pastorek², Stanislava Fintova³, Branislav Hadzima⁴

¹ Department of Materials Engineering, Faculty of Mechamical Engineering, University of Zilina, Slovakia

² Research Centre, University of Zilina, Slovakia

³ Institute of Physics of Materials, Academy of Sciences of the Czech Republic, Brno, Czech Republic

⁴ Department of Materials Engineering, Faculty of Mechamical Engineering, University of Zilina, Slovakia and Research Centre, University of Zilina, Slovakia

The effect of mechanical and chemical surface treatment of high-strength low alloy steel S355J2 on its electrochemical characteristics was investigated by voltamperic tests in corrosive environment of 0.1M NaCl solution simulating sea atmosphere. Mechanical surface treatment was done by grinding on 1200 grit paper and by sandblasting. Chemical surface treatment was performed by iron phosphating in aqueous solution of H3PO4 and FeCl3.6H2O. Thermodynamic and kinetic corrosion characteristics including corrosion potentials and corrosion current densities were measured and analysed by potentiodynamic polarisation curves and Tafel analyses respectively. The positive combination of these two techniques on corrosion properties of S355J2 steel surface was reported.

Keywords: S355J steel; corrosion properties; iron phosphating; surface treatment